Injection molding grade HIPS pellets Black HIPS granule plastic raw material

Share on:


Price:
Price in USD:Details

Quantity:


Product Overview

Description


High impact polystyrene (HIPS), as ecru opaque particles.With high impact strength and toughness.Can be any color, molding processability, resistance to chemical corrosion, electric performance is very good also. HIPS: can injection or extrusion shaped into a variety of products, injection temperature is 160-180 degrees, the pressure of 70 mpa.


 1.jpg2.jpg3.jpg



Application


HIPS


    The material can be used as packaging filler, pressed into board, molded into products, or delivered on sheets or rolls. Its characteristic dimensional stability permits it to be employed in low strength construction, and in its natural translucent form makes it suitable for food processing applications.


 












































































Properties



ASTM method



Test Condition



Unit



Typical Value



Specific Gravity



D542



---



---



1.046



Melt Flow Index



D1238



200°C,5 kg load



g/10 min



4.6



Tensile Strength at Yield



D638



23°C,1/8” Sample



kg/cm2



300



Elongation at Break



D638



23°C,1/8” Sample



%



40



Izod Impact Strength



D256



23°C,A method,notched1/8”×1/2”×5/2”



kg/m2



9.5


 



Vicat Softening Temperature



D1525



1 kg load,3 mm Thick ( 120°C/hr )



°C



97



Flammability



UL-94



1/16” Sample



File No.E50263



94HB



Residual SM monomer



---



---



ppm



<300



Yellow Index



---



---



---



-6



 


Package & Storage:
1. Packing: 25Kg/bag internally film-coated polypropylene woven bags. 
2. Storage : The resin should be stored in a drafty, dry warehouse and away from fire and direct sunlight. It should not be piled up in the open air. 
3. Transportation : During transportation, the product should not be exposed to strong sunlight or rain and should not be transported together with sand, soil, scrap metal, coal or glass. 