6mm 8mm 10mm 13mm 16mm al2o3 porous porcelain beads ceramic balls as supporting material

 

 

Product Description

porous ceramic ball-1.jpg

Porous ceramic balls not only support and cover the catalyst, but also filter and eliminate the impurities.

Porous ceramic balls are also called filtering balls. They are made by drilling on the inert ceramic balls. Therefore it can be used for not only supporting and covering the catalyst, but also filtering and eliminating the impurities of grain, gelatin, asphaltine, heavy metals or iron ions, etc, which is less than 25µm. When the porous balls are set on the top of the reactor, the impurities which failed to be eliminated in former process could be absorbed in the pores of the ceramic balls, thereupon protect the catalyst and prolong the operating cycle of the system.

 

Type Feldspar Feldspar-Molai Molai Stone Molai-Corundum Corundum
Chemical Ingredients (%) Al 2O3 20-30 30-45 45-70 70-90 ≥90
Al2O3 +SiO2 ≥90
Fe2O3 ≤1
Water Adsorption(%) ≤5
Acid Resistance(%) ≥98
Alkaki Resistance(%) ≥80 ≥82  ≥85  ≥90 ≥95
Operation Temperature(°C) ≥1300 ≥1400 ≥1500 ≥1600 ≥1700
Crushing Strength(N/pcs) Φ6 ≥400 ≥420 ≥440 ≥480 ≥500
Φ8 ≥480 ≥520 ≥600 ≥620 ≥650
Φ10 ≥600 ≥700 ≥800 ≥900 ≥1000
Φ13 ≥1000 ≥1100 ≥1300 ≥1500 ≥1800
Φ16 ≥1500 ≥1600 ≥1800 ≥2300 ≥2600
Φ20

≥1800

≥2000 ≥2300 ≥2800 ≥3200
Φ25 ≥2500 ≥2800 ≥3200 ≥3600 ≥4000
Φ30 ≥3000 ≥3200 ≥3500 ≥4000 ≥4500
Φ38

≥4000

≥4500 ≥5000 ≥5500 ≥6000
Φ50

≥6000

≥6500 ≥7000 ≥8500 ≥10000
Φ60

≥8000

≥8500 ≥9000 ≥10000 ≥12000
Φ75 ≥10000 ≥11000 ≥12000 ≥14000 ≥15000
Bulk Density (kg/m3) 1100-1200 1200-1300 1300-1400 1400-1550 ≥1550
Diameter 6   8    10 13 16 20 25 30  38  50 60   75
Tolerance of diameter(mm) ±1.0 ±1.5 ±2.0 ±3.0
Pore diameter(mm)

2~3

3~5 5~8 8~10

 

Application:
It is developed on the basis of inert ceramic ball. It has an adequate mechanical strength, good chemical and thermal stability as the normal inert ceramic ball, further more, it has larger surface area and free void which directly make the dispersion and flux of the fluids increased, and bring down the resistance of the system resulting from the perforated holes on the ball. As a new efficient support and covering material of catalyst, it has been widely used in oil refinery, chemical, fertilizer, natural gas and environment protection industries since put into market .

 