Virgin HDPE High Density Polyethylene Granules/ PE 100 PE80 Black /HDPE PE 100 Virgin& Black Pipe Grade

TYPICAL APPLICATIONS

for pressure pipe, for gas and water distribution, sewage and drainage.

Physical

Method

Unit

 
Value

Density

ISO 1183

g/cm3

0.959

Melt Flow Rate (190°C /5kg)

ISO 1133

g/10 min

0.23

Melt Flow Rate (190°C /21.6kg)

ISO 1133

g/10 min

6.4

Staudinger Index Jg

ISO 1628

Ml/g

380

Vicat Softening Temperature(VST/B/50 K/h (50N))

ISO 306

°C

74

Mechanical

Mechod

Unit

 
Value

Tensile Modulus (23°C, v = 1mm/min, Secant)

ISO 527-1, -2

MPa

900

Tensile Stress @ Yield (23°C, v = 50 mm/min)

ISO 527-1, -2

MPa

23

Tensile Strain @ Yield (23°C, v = 50 mm/min)

ISO 527-1, -2

%

9

Tensile Creep Modulus 1h [Test stress in MPa]

ISO 899-1

MPa

850 [2.0]

Tensile Creep Modulus 1000h [Test stress in MPa]

ISO 899-1

MPa

360 [2.0]

Maximum Elongation TD

EN 638

%

>350

MRS Classification

ISO/TR 9080

MPa

10

Flexural Stress at 3,5% deflection

ISO 178

MPa

21

FNCT (4.0 MPa, 2% Arkopal N 100, 80°C)

ISO 16770

h

>1000

Flexural Creep Modulus
(4 Point loading method, 1 min-value)
(4 Point loading method, 24 h-value)
(4 Point loading method, 2000 h-value)

DIN 19537-2

 
MPa
MPa
MPa

 
1100
560
330

Charpy Notched Impact Strength
(23°C)
(-30°C)

ISO 179

 
kJ/m2
kJ/m2

 
26
13

Shore Hardness (Shore D (3 sec))

ISO 868

63

Oxidation Induction Time (OIT) (210°C)

EN 728

min

30

Carbon Black Content

ISO 6964

%

2.25

Odour Treshold

EN1622/EN1240

<2