High strength abrasion resistance flexible two-component urethane resin MU-697A/MU-697B
MU-697 is a two-component (Part A, Part B) polyurethane elastomer resin product.
It has excellent elasticity and toughness against vibration, abrasion, and compression.
Due to its excellent fluidity, it can be used for various applications such as embedding and fixing, molding, etc.
It can be used for a wide range of applications which require an elasticity, such as shoe soles, rubber vibration isolator, rubber rollers, rubber cushions for OA floors, and packing for general use.
It is safe because it does not contain MOCA like urea rubber.
Polyurethane is, due to its low halogen, environment friendly.
This product contains NO mercury and fully complaint for RoHS regulation.
In addition, it has no plasticizer, so it can reduce bleeding which may affect to surrounding components.
(4) Product information
As supplied （Typical Value）
Item | Condition | Unit | MU-697A | MU-697B | ||
Appearance | visual | － | Colorless semitransparent | Light yellow transparent | ||
Specific Gravity | 25℃ | － | 0.99 | 1.12 | ||
Viscosity | 25℃ | mPa・s | 190 | 560 | ||
Mixing Ratio | parts by weight | 100/200 | ||||
Mixed Viscosity | 25℃ | mPa・s | 450 | |||
Pot Life | 25℃, cup, 100g | minute | 4 minutes 30 sesonds | |||
Gel Time | room temp., cup, 100g | minute | 10 minutes | |||
Demold Time | room temp., cup, 100g | minute | 30 minutes | |||
Item | Condition | Unit | Typical Value |
Appearance | visual | ー | White |
Hardness | 25℃ | Shore A | 80 |
Tensile Strength | dumbbell No.2 | MPa | 35 - 40 |
Elongation | dumbbell No.2 | ％ | 450 - 500 |
Tear Strength | dumbbell No.2 | N/mm2 | 50 - 55 |
Taber Abrasion | 9. 8N, 1000 times, H22 | mg | 70 |
*Curing conditions : 60℃ - 1hrs + 40℃ - 24hrs
This product is made in Japan.
Please contact us for details.
According to some country and regional regulation regarding chemical substances, this product may not be exported.
・Keep in mind that if water was included in the mixing process, it will cause foaming and uncured.
・When color a resin, add pigment into part A at first, and stir evenly before use.
・If resin was crystallized, heat the resin at 60~80℃ for 30~60 minutes, and use it after the crystallized part melt. Please stop using the resin when you see crystalized part left even after the heating.
1. Calculate the weight of part A and part B to mix, according to the mixing ratio designated in product information.
2. At first, weigh part B in a plastic cup, then put part A into the same cup. Please do not use a paper cup, because paper cup often has the moisture on the surface which may cause foaming.
3. Stir well part A with part B in the plastic cup. Please use a stirring bar or mixer. We recommend use a metal or plastic flat bar.
4. Stir well at the bottom and corner of the cup.
5. After stirring, defoam mixed resin immediately.
6. After defoaming, pour the resin into a case and cure it by standard curing schedule. Please note that poured resin may cause foaming if there is water or moisture on the surface of a case.
Company Profile
PELNOX, LTD.
We are a formulator of resin compounds and adhesives manufacturing company, offering more than 900 products to more than 1,000 companies around the world.We can assist the customers where needed, from the small quantity prototype stage, up to the development of resin products. That is a wide range of materials including epoxy liquids and powders, urethane, silicone, and conductive paste materials.
We Recommend
New Arrivals
New products from manufacturers at wholesale prices