Чистый полиэтилен низкой плотности LDPE 2426h в гранулах LDPE

Чистый полиэтилен низкой плотности LDPE 2426h в гранулах LDPE

Category: LDPE >>>
Supplier: B.S.M,TRADING,COMPANY,LIMITED

Price:

Price in USD:Details

Quantity:

Product Overview

Description

AVAILABLE TYPES

1- LDPE STRETCH FILM SCRAP
2- LDPE FROM WASTE INDUSTRIAL FILM
3- LDPE MIXED POST-INDUSTRIAL & POST-COMMERCIAL
4- LDPE 99/1 SCRAP WASTE FILM
5- LDPE 98/2 WASTE POST-CONSUMER SCRAP NATURAL COLOR
6- LDPE 95/5 STRETCH FILM WRAP FROM PACKAGING
7- LDPE 90/10

=========================================

Virgin LDPE 2426H LDPE Granules Low Density Polyethylene price

1. Description:
LDPE/Low Density Polyethylene is for injection molding.
LDPE has excellent rheology or molten liquid.

2. Application:
Used for manufacturing agricultural film, shrink film, hyaline membrane, shopping
Bag, packing bag.

LDPE Film Grade

Tests	Value	Unit
Melt Flow Rate (MFR)	1	g/10min
Density	0.922	g/cm3
Tensile Yield Strength	7	Mpa
Elongation at Break	75	%
Wien Softening Point	85	°C
Packing	In 25 kg PP woven bags,20MT/20’FCL

LDPE Injection grade:

Tests	Value	Unit
Melt Flow Rate (MFR)	2	g/10min
Density	0.9225	g/cm3
Tensile Strength	9	Mpa
Elongation at Break	500	%
Fish eye max(0.3-2mm)	30	n/1200cm2
Stripes	20	cm/20m3
Packing	In 25 kg PP woven bags,20MT/20’FCL

Specification

Product name	Virgin LDPE Resin Granules
Type	Plastic Raw Materials Granules Resins
Color	Transparent
Shape	Pellet - Granules
Application	Packaging of all kinds of articles
DENSITY	0.924 g/cm3
MFR	0.6 - 0.8 G/10 Min
Melting point	110~115℃
Processing	150~210℃
Model	BS2021-LDPE

LDPE:

Physical Properties		Test Method	Nominal Value	Unit
Density		ISO 1183	0.921	g/cm3
Melt Mass-Flow Rate (MFR)		ISO 1133	1.9	g/10min
Hardness
Shore Hardness (shore D)		ISO 868	45
Mechanical Properties
Tensile Modulus		ISO 527-2	175	MPa
Tensile Strength	Yield,	ISO 527-2	9.0	MPa
Tensile Strength	Break,	ISO 527-2	13.0	MPa
Tensile Strain(Break)		ISO 527-2	850	%
Modulus of Elasticity		Internal Method	250	MPa
Thermal
Vicat Softening Temperature		ISO 306/A50	89.0	°C
Melting Temperature (DSC)		DIN 53765	108	°C
Peak Crystallization Temperature (DSC)		DIN 53765	97.0	°C
Heat of Fusion		DIN 53765	110	J/g
Electrical
Volume Resistivity		ASTM D257	8.5E+15	ohm •cm
Dielectric Strength		ASTM D149	30.0	kV/mm
Dielectric Constant (60Hz)		ASTM D150	2.20	%
Dissipation Factor (60 Hz)		ASTM D150	0.00050

LLDPE

Properties	Test conditon	Test method	Test data	Unit
Density			0.91
MFI			2
Drop impact strength		ASTM D-1709	90	g
Elongation ,vertical/horizontal		ASTM D-882	600/800	%
tensilestrength,thermal resistance		ASTM D-1004	105/95	Kg/cm
elongation		ASTM D-638	930	%
tensile strength		ASTM D-638	180
tensile strength,vertical/horizontal		ASTM D-882	380/350
Vicat softening point		ASTM D-1525	103	°C
melting point		ASTM D-2117	126	°C
Turbidity		ASTM D-1009	12	%
45 glossness		ASTM D-2457	75	%