transparent resin marine arts and crafts for manufacturing FRP fishing boats, yachts, lifeboats and other large shaped products

Product Overview

Description

 

Product description

1) It is a solution of o-benzene type unsaturated polyester resin in styrene, with accelerant and thixotropic agent added
Low reaction exothermic temperature, good construction performance. It has good water resistance and excellent mechanical strength, which is suitable for FRP fishing
Ships, yachts, lifeboats and other large shaped products;
2) It has been approved by Lloyd's, China Classification Society and Japan Maritime Association;
3) TC-K909CC (n) w is suitable for winter use from November to February (below 15 ℃);
TC-K909CC (n) m belongs to spring and autumn type, which is suitable for March to May and September to October (15-25 ℃);
TC-K909CC (N) S belongs to summer type, which is suitable for June to August (above 25 ℃);
TC-K909CC-W, TC-K909CC-M and TC-K909CC-S contain wax and have air dryness;
TC-K909CC-(N)W, TC-K909CC-(N)M and TC-K909CC-(N)S do not contain wax and are non air drying.

 

 Technical index of liquid resin

Item	TC-K909CC-(N)W	TC-K909CC-(N)M	TC-K909CC-(N)S	remarks
viscosity(Pa.S)	0.15-0.29	0.26-0.40	0.30-0.50	test method
Thixotropy index	1.2-2.8	1.2-2.8	1.2-2.8	JIS-K-6901
Gelation time*(min.)	10.0-24.0	15.0-45.0	25.0-55.0	*55%MEKP:1%

 

Physical properties of casting body and FRP

                 

Item	Measured value		Test method
	Casting body	FRP
proportion	1.2	--	JIS-K-7112
Shrinkage rate (%)	7.8	--	Recalculation based on liquid / solid ratio
Hot deformation temperature (℃)	65	--	JIS-K-7207
Water absorption rate (%)	0.22	0.17	JIS-K-7209
Barco hardness (hbi-a)	42	45	JIS-K-7060
Tensile strength (MPA)	62	107	JIS-K-7113
Tensile modulus (MPA)	3900	8800	JIS-K-7113
Tensile elongation (%)	2	--	JIS-K-7113
Bending strength (MPA)	120	191	JIS-K-7203
Bending modulus (MPA)	3800	6800	JIS-K-7203
Compressive strength (MPA)	137	142	JIS-K-7208
Hammer impact strength (kJ / m2)	2.1	--	JIS-K-7111
V-type impact strength (kJ / m2)	--	--	JIS-K-7110
Glass fiber content (%)	--	30.1s	JIS-K-7052

 

Remarks:

1) Curing agent dosage: 55% MEKP 1%;
2) Casting body: 3mm thick, post curing at 110 ℃ for 2 hours;
3) FRP: 3 layers of chopped mat (450g / m2), and then cured at 40 ℃ for 16 hours.

 

Liquid resin package and storage conditions

 

1.Packed in metal barrel , 220kg/barrel (about 55 gallons)
2. Try to prevent liquid resin from directly sunshine and heat resource
3 Prohibit open before use
4. Flammable, should keep away from open fire
5. Shelf life is 3-6 month under 25℃
6. Store and operate in a dry, well-ventilated place
7. Please read MSDS carefully before use this product

 

1. Q: Is your company a manufacturer?

     A: Yes,we are. At the same time, we are also agents of other product brands.

 

2. Q:  Does your company provide samples?

     A:  Yes,If you have a shipper in China ,sample will sent to him freely .

 

3. Q:How long could the resin be stored ?

     A: Normally , 90 days .but if promoted resin ,it's about 45 days .

 

4. Q: If I will get a better price with big QTY ?

    A: Of course , best price will be granted u as per QTY.