BRAND: | SHENMA | GRADE: | PA6 1330 BK1082 |
MATERIAL: | PA6+15%GLASS FIBER | ||
APPEARANCE: | WHITE | ||
FORM: | PELLETS | ||
PROCESSING METHOD: | INJECTION MOLDING |






Test Condition | Test Method | Unit | Typical Value | |
Physical | ||||
Density | ISO 1183 | kg/cm3 | 1236 | |
Shrinkage | ISO 2577 | % | 0.6-1.4 | |
Ash Content | ISO 3451-4 | % | 15 | |
Melt Temperature(DSC) | ISO 11357-1/-3 | ℃ | 220 | |
Mechanical | ||||
Tensile Modulus | ISO 527-1/-2 | Mpa | 6,300 | |
Tensile Strength | ISO 527-1/-2 | Mpa | 120 | |
Elongation at Break | ISO 527-1/-2 | % | 3 | |
Flexural Modulus | ISO 178 | Mpa | 5,000 | |
Flexural Strength | ISO 178 | Mpa | 180 | |
Charpy Notched Impact Srength | 23℃ | ISO 179/leA | KJ/m² | 7 |
Thermal | ||||
HTD | 1.80Mpa | ISO 75-1/-2 | ℃ | 190 |
Flammability | UL-94 | |||
1.6mm | HB |