Product name | ABS Pellets | |||||
Synonyms | ABS particle | Model NO. | D-2200 D-2400 | |||
Certificate | ISO SGS | Type | heat-resisting | |||
Appearance | Micky grain | MFR((220℃, 10kg ) | 6 - 10.5 cm 3 /10min | |||
MOQ | 25KG | MFR(200℃,5kg) | / | |||
CAS | 9003-56-9 | Feature | Impact resistance, heat resistance, low temperature resistance, etc |
特性(Properties) | 測試方法 (Test Method) | 測試條件 (Test Condition) | 單位 (Unit) | D-2200 | D-2400 |
引張強度 Tensile Strength | ISO 527 | 50 mm/min | MPa | 37 | 43 |
延伸率 Tensile Elongation | ISO 527 | 50 mm/min | % | 40 | 40 |
彎曲強度 Flexural Strength | ISO 178 | 2mm/min | MPa | 56 | 65 |
彎曲彈性率 Flexural Modulus | ISO 178 | 2 mm/min | GPa | 2.0 | 2.4 |
IZOD 衝擊強度 Izod Impact Strength | ISO 180 | 4mm/23℃ | kJ/m2 | 14 | 16 |
Charpy 衝擊強度 Notched Impact Strength | ISO 179 | 4mm/23℃ | kJ/m2 | 15 | 15 |
流動係數(MFR) Melt Flow Index | ISO 1133 | 200℃,5kg | cm3/ 10min | / | / |
220℃,10kg | 15 | 7.0 | |||
硬度Hardness | ASTM D785 | - | - | R-110 | R-115 |
密度Density | ISO 1183 | 23℃ | g/cm3 | 1.05 | 1.06 |
軟化點 Vicat Softening Temp. | ISO 306 | 10N,50℃/hr | ℃ | 112 | 118 |
熱變形溫度 Heat Distortion Temp. | ISO 75-2 | 1.8MPa annealed | ℃ | 104 | 112 |
1.8MPa unannealed | 86 | 92 | |||
燃燒率Flammability | File No.E194560 UL&C-UL | - | - | 1.5mm HB | 1.5mm HB |
收缩率 Shrinkage | ISO 294-4 | % | 0.3 ~ 0.6 | 0.3 ~ 0.6 |