Physical properties of | rating | Unit | The test method | |
The density of | ||||
---3 | 1.07 | g/cm³ | ASTM D792 | |
23℃ | 1.07 | g/cm³ | ISO 1183 | |
Melt mass flow rate | 4.0 | g/10min | ASTM D1238 | |
Volume flow rate of solution | 4.50 | cm³/10min | ISO 1133 | |
shrinkage | 0.30到0.60 | % | ISO 294-4 | |
Impact properties | rating | Unit | The test method | |
Notched impact strength of simply supported beam | ISO 179 | |||
-30℃ | 6.0 | KJ/㎡ | ISO 179 | |
23℃ | 13 | KJ/㎡ | ISO 179 | |
Notched impact strength of cantilever beam | ||||
23℃,3.2mm | 120 | J/m | ASTM D256 | |
23℃,6.4mm | 110 | J/m | ASTM D256 | |
-30℃ | 6.0 | KJ/㎡ | ISO 180-1A | |
23℃ | 12 | KJ/㎡ | ISO 180-1A | |
Thermal performance | rating | Unit | The test method | |
Thermal deformation temperature | ||||
1.8MPa,Without annealing | 109 | ℃ | ASTM D648 | |
1.8MPa,Without annealing | 101 | ℃ | ISO 75-2/A | |
1.8MPa,annealing | 120 | ℃ | ASTM D648 | |
1.8MPa,annealing | 121 | ℃ | ISO 75-2/A | |
VEKA softening temperature | ||||
A50 | 129 | ℃ | ISO 360/A50 | |
B50 | 121 | ℃ | ISO 306 | |
Linear coefficient of thermal expansion | ||||
MD | 8.2E-5 | 1/℃ | ISO 11359-2 | |
Flame retardant performance | rating | Unit | The test method | |
Flame retardant grade | ||||
1.50mm | HB | UL 94 | ||
Mechanical properties of | rating | Unit | The test method | |
Rockwell hardness | ||||
Rated R | 115 | ASTM D785 | ||
The tensile strength | ||||
yield 4 | 44.0 | MPa | ASTM D638 | |
yield | 45.0 | MPa | ISO 527-2/50 | |
The fracture | 32.0 | MPa | ISO 527-2/50 | |
Tensile strain | ||||
The fracture 4 | 10 | % | ASTM D638 | |
The fracture | 29 | % | ISO 527-2/50 | |
Bending modulus | ||||
--5 | 2210 | MPa | ASTM D790 | |
--6 | 2300 | MPa | ISO 178 | |
The bending strength | ||||
--5 | 68.3 | MPa | ASTM D790 | |
--6 | 74.0 | MPa | ISO 178 |