spray Polyurea Protective Coating For Aviation industry spray system

Product Overview

Description

 

Special protection is required for satellites and rockets in aviation industry, as common material is inadequate. SWD Company developed an special polyurea coating whose high quality has been well approved, used for satellites and rockets with perfect performance. 

                                                                                

Characteristics            

The product has high reactivity, could spray-applied forming on curved,slope and vertical surface without sagging. Insensitive to moisture and temperature. No peeling and cracking when against the impact of cold and hot circumstances. Flexible and dense coating has strong adhesion to various substrates like metal and PU insulation materials. High performance of impact and wear resistance, no pulverization when long term use outdoors. A green product, no harm to human.

                                                                                

Specifications 

Adhesive strength (PU rigid foam substrate)                  2.3Mpa

Adhesive strength (steel sheet substrate)                    13.5 Mpa

Tear strength                                                                      81kN/m

Tensile strength                                                                18Mpa

Elongation                                                                         470%

Anti-permeability                                                                2.8Mpa

Applicable Temperature variation                                -40------+130℃

Wear resistance  (700g/500r)                                     5mg

Acid resistance (10%H2SO4 or 10%HCI, 30d)              no corrosion no bubbles no peeling

Alkali resistance 10%NaOH, 30d                         no corrosion no bubbles no peeling

Salt resistance 30g/L, 30d                                  no corrosion no bubbles no peeling

Salt spray resistance 2000h                               no corrosion no bubbles no peeling

Oil resistance 0# diesel crude oil 30d               no corrosion no bubbles no peeling

                                                                               

Basic data

Color                                    Multiple colors as customers’ needs

Gloss                                    Yes

Density                                 1.02g/cm3

Volume solids content            99%±1%

VOC                                      0

Recommended dry film thickness   2000-3000μm

Theoretical coverage            2.04kg/sqm (calculated by the above solids percentage and dry film thickness of 2000 microns)

Practical coverage                     Allow appropriate loss rate

Surface Dry time                       5-20s

Overcoating interval                  min: 1h, max: 24h

Application method                  Special polyurea sprayer

Flash point                               200℃

                                                                               

 

Recommended solutions

No.	Name of products	Layers	Dry film thickness(μm)
1	SWD polyurea special primer	1	50
2	SWD 9006	1	2500
Total		2	2550

 

 

Application scope           aviation industry equipment     

 

Shelf life                  6 months (Indoor with dry and cool conditions)                                                                               

 

Packing                    Component A: 220kg/bucket, component B: 200kg/bucket

 

                                                              