EVA18% | |||
Properties | Test method | Value | |
VA Content(%) | USI | 18 | |
Density(g/cm3) | ASTM D792 | 0.939 | |
Melt Index (g/10min) | ASTM D1238 | 2.5 | |
Tensile Strength(Molded)(Break)(kg/cm2) | ASTM D638 | 180 | |
Ultimate elongation(Molded)(%) | ASTM D638 | 750 | |
Low Temperature Brittleness(℃/F50) | ASTM D746 | <-76 | |
Vicat Softening Point(℃) | ASTM D1525 | 64 | |
Melt Point (℃) | ASTM D3418 | 86 | |
Hardness(Shore D) | ASTM D2240 | 36 | |
EVA28% | |||
PROPERTIES | TEST METHOD | UNIT | Data |
VA Content | % | 28.0 | |
Density | ASTM D1505 | g/cm3 | 0.954 |
Melt Index MI2.16 | ASTM D1238 | g/10min | 15 |
Tensile Strength (Break) | ASTM D638 | Kg/cm2 | 80 |
Elongation at break | ASTM D638 | % | >800 |
Melting point | ASTM D-3418 | ℃ | 69 |
Hardness | ASTM D2240 | Shore D | 20 |