Economic TGIC Polyester Resin with Outstanding Leveling Performance
- Category: >>>
- Supplier: Guangzhou Kinte Industrial Co. Ltd.
Share on (1600569556826):
Product Overview
Description
Products Description
Introduction
NH0307 is a saturated polyester resin designed for both TGIC and HAA powder coating systems.
With the improvement of human living standards, people's awareness of green environmental protection is getting stronger and stronger, and powder coatings have achieved rapid development due to their high efficiency, environmental protection and economic advantages.
Powder coatings are required to be stored in a ventilated, dry and clean environment below 30°C, not close to fire sources and heating, avoid direct sunlight, and prevent rain or sunlight exposure during product transportation.
In the rainy season or hot summer, due to the humid environment and excessively high temperature, powder coatings are prone to agglomeration during manufacturing, storage, transportation and use, resulting in gun guns and empty guns during powder spraying, which seriously It affects the powder coating rate and the surface smoothness of the coating film.
NH0307 has a high tg, so the powder coatings prepared with it have excellent storage stability, avoiding the above problems.
With the improvement of human living standards, people's awareness of green environmental protection is getting stronger and stronger, and powder coatings have achieved rapid development due to their high efficiency, environmental protection and economic advantages.
Powder coatings are required to be stored in a ventilated, dry and clean environment below 30°C, not close to fire sources and heating, avoid direct sunlight, and prevent rain or sunlight exposure during product transportation.
In the rainy season or hot summer, due to the humid environment and excessively high temperature, powder coatings are prone to agglomeration during manufacturing, storage, transportation and use, resulting in gun guns and empty guns during powder spraying, which seriously It affects the powder coating rate and the surface smoothness of the coating film.
NH0307 has a high tg, so the powder coatings prepared with it have excellent storage stability, avoiding the above problems.
Basic Features
High cost-performance
Excellent storage stability
Outstanding leveling performance
Recommend Formulation
NH0307——TGIC | ||||||||||||
NH0307 | TGIC | Filler ＆ pigment | Leveling agent | Benzoin | 701 | 703 | ||||||
300 | 22.6 | 190 | 4 | 2 | 2.5 | / | ||||||
NH0307/HAA | ||||||||||||
NH0307 | T-105 | Filler ＆ pigment | Leveling agent | Benzoin | 701 | 703 | ||||||
300 | 15.8 | 190 | 4 | 2 | 2 | 2 | ||||||
Specifications I
Appearance | white or pale yellow transparent flakes |
Acid Number (mgKOH/g) | 30～36 |
Softening Point (℃) | 105～115 |
Glass Transition Temp. (℃) | ～63 |
Melting Viscosity (200℃, ICI, mPa·s) | 3600±800 |
Reactivity at 180℃ (s, 7% TGIC) | 240±100 |
Curing Requirement | 200℃×10min (TGIC) 180℃×10min (HAA) |
Packaging | PE Bags, Net Weight 25kg ± 0.1kg / bag |
Specifications II
Extrusion Condition | Two-screw Extruder | ||
Jacket temperature | 100～110℃ | ||
Speed of Revolution | 500～1200rpm | ||
Fineness of Powder | ＜100μm | ||
Application Condition | Electrostatic Spraying With | 40～70KV | |
Coating Film Thickness | 60～80μm | ||
Degreased Cold-rolled Steel | 0.5mm | ||
Film Properties | Gel Time (180℃, sec) | 300~450 | |
Horizontal Flow (180℃, mm) | 26~30 | ||
Gloss (60°) | ≥80% | ||
Adhesive (1mm, grade) | 0 | ||
Pencil Hardness | ≥1H | ||
Impact (50cm) | pass | ||
Package and Transportation
PE Bags, Net Weight 25kg ± 0.1kg / bag, 875Kg/Pallet, 17,500Kg/20GP
Non-dangerous goods, no special transportation requirements.