Best price Polymethyl methacrylate PMMA powder
US $2.80-$3.80
Share on:
Properties | ISO Test Method | Test Condition | Unit | CM-205 |
Melt Flow Index | 1133 | 230ºC×3.8KG | ml/10 min | 1.9 |
Mass Density | 1183 | 23 ºC | g/cm3 | 1.19 |
Tensile Strength | 527 | 5 mm/min, yield | MPa | 70 |
5 mm/min, break | MPa | 70 | ||
Tensile Elongation | 527 | 50 mm/min | % | 12 |
Flexural Strength | 178 | 2 mm/min | MPa | 103 |
Flexural Modulus | 2 mm/min | GPa | 2.8 | |
Izod Impact Strength | 180/1A | 23 ºC Notched | KJ/m2 | 2 |
-30 ºC Notched | KJ/m2 | - | ||
Charpy Impact Strength | 179 | 23 ºC Notched | KJ/m2 | 2 |
-30 ºC Notched | KJ/m2 | - | ||
Vicat Softening Temp. | 306 | 1 Kg,50 ºC/hr | ºC | 115 |
5 Kg,50 ºC/hr | ºC | 107 | ||
Heat Distortion Temp. | 75/A | 1.8 MPa Unannealed | ºC | 95 |
1.8 MPa Annealed | ºC | 104 | ||
Coefficient of Linear Thermal Expansion | 11359 | - | - | 6 X 10-5 |
Flammability | - | UL-94 | - | 1.5mm HB |
Mold Shrinkage | 294-4 | - | % | 0.2~0.6 |
Symbol | 1043 | - | - | >PMMA< |