Share on (1600688094744):
BRAND: | BLUESTAR | GRADE: | 403GM30 | ||
MATERIAL: | PBT+30% GLASS FIBER AND MINERAL REINFORCED | ||||
FEATURES: | 1. FLAME RETARDANT | 2. HIGH THERMAL STABILITY AND GOOD PROCESSABILITY | 3. HIGH GLOW-WIRE IGNITION TEMPERATURE | ||
COLOR: | CUSTOMIZED | ||||
FORM: | PELLETS | ||||
METHOD: | INJECTION MOLDING |
Properties | Test Condition | Test Method | Unit | Typical Value |
Physical | ||||
Specific Gravity | ISO1183-1-2012 | g/cm³ | 1.66 | |
Molding Shrinkage (Parallel) | ISO 294-4 | % | ||
Melt Flow Rate | 250℃/2.16kg | ISO1133:2011 | g/10min | 30 |
Mechanical | ||||
Tensile Stress at break | 10mm/min | ISO 527-2 | mpa | 90 |
Tensile Strain at break | 10mm/min | ISO 527-2 | % | |
Flexural Strength | 2mm/min | ISO 178:2010 | mpa | 160 |
Flexural Modulus | 2mm/min | ISO 178:2010 | mpa | 8,500 |
Charpy Impact | Notched, 23℃ | ISO 179 | kj/m² | 6 |
Charpy Impact | Unnotched, 23℃ | ISO 179 | kj/m² | 40 |
Thermal | ||||
Heat Deflection Temperature | 1.80Mpa, 3.2mm, unannealed | ISO 75-1/-2 | ℃ | 208 |
Heat Deflection Temperature | 0.45Mpa, 3.2mm, unannealed | ISO 75-1/-2 | ℃ | 220 |
Flammability | 0.38-1.6mm | UL94 | - | V-0 |
Glow-wire Ignition Temperature | IEC 60695 | ℃ | 775 | |
Electrical | ||||
Volume Resistivity | IEC 60093 | Ω.cm | 1.1×1016 | |
Dielectric Strength, in oil | IEC 60243-1 | KV/mm | 20 |