Physical Properties | Test Method | Nominal Value | Unit | ||
Density | ISO 1183 | 0.921 | g/cm3 | ||
Melt Mass-Flow Rate (MFR) | ISO 1133 | 1.9 | g/10min | ||
Hardness | |||||
Shore Hardness (shore D) | ISO 868 | 45 | |||
Mechanical Properties | |||||
Tensile Modulus | ISO 527-2 | 175 | MPa | ||
Tensile Strength | Yield, | ISO 527-2 | 9.0 | MPa | |
Break, | 13.0 | MPa | |||
Tensile Strain(Break) | ISO 527-2 | 850 | % | ||
Modulus of Elasticity | Internal Method | 250 | MPa | ||
Thermal | |||||
Vicat Softening Temperature | ISO 306/A50 | 89.0 | °C | ||
Melting Temperature (DSC) | DIN 53765 | 108 | °C | ||
Peak Crystallization Temperature (DSC) | DIN 53765 | 97.0 | °C | ||
Heat of Fusion | DIN 53765 | 110 | J/g | ||
Electrical | |||||
Volume Resistivity | ASTM D257 | 8.5E+15 | ohm •cm | ||
Dielectric Strength | ASTM D149 | 30.0 | kV/mm | ||
Dielectric Constant (60Hz) | ASTM D150 | 2.20 | % | ||
Dissipation Factor (60 Hz) | ASTM D150 | 0.00050 | |||