Physical properties | rating | Units | Test methodology |
density | 0.9 | g/cm³ | |
Apparent density | 0.48 to 0.52 | g/cm³ | |
Melting rate (melt flow rate) (230°C/2.16 kg). | 2.9 to 3.5 | g/10 min | ASTM D1238 |
Ash content | 0.025 to 0.050 | % | |
Gel content 1 | |||
> 200.0 µm | 500 | pcs/m² | |
0.700 to 1.50 mm | 50 | pcs/m² | |
1.50 to 2.50 mm | 3 | pcs/m² | |
> 2.50 mm | 0 | pcs/m² | |
Rockwell hardness (R grade). | 82 to 95 | ||
Mechanical property rating unit system test method | |||
Tensile strength (yield). | 34 | MPa | ASTM D638 |
Elongation (yield). | 10 | % | ASTM D638 |
Flexural modulus | 1400 | MPa | ASTM D790 |
Thermal performance rating unit system | |||
Vicat softening temperature 3 | 150 to 154 | °C |