Test Item | Test Method | Test Condition | Unit | Test Value |
MFR | GB/T 3682.1 | 200℃/5kg | g/10min | 8 |
Tensile fracture stress | GB/T 1040.2 | 50mm/min | MPa | 48 |
Nominal fracture strain | GB/T 1040.2 | 50mm/min | % | 2 |
flexural modulus | GB/T 9341 | 2mm/min | MPa | 3100 |
bending strength | GB/T 9341 | 2mm/min | MPa | 79 |
CHARPY Impact Strength | GB/T 1043.1 | 23℃/1eU | kJ/m2 | 9 |
Vicat Softening Temperature | GB/T 1633 | B50 | ℃ | 91 |
distortion temperature | GB/T 1634.2 | 0.45MPa | ℃ | 85 |
Density | ISO1183-1 | kg/ m3 | 1040 | |
VLT | GB/T 2410 | % | 90 | |
water absorption | ISO62 | % | <0.1 | |
UL flammability | UL 94 | Class | 94HB | |
Shrinkage rate of molding products | GB/T 17037.4 | % | 0.3-0.4 |