Product Overview
Description
Product Description
High temperature resistance hermoplastic TPU Film
Advatage
- Excellent abrasion resistance
- High tear resistance
- Low temperature flexibility
- High temperature resistance
- Excellent Elongation and tensile strength
- Environmentally friendly
- Various hardnesses
- Long-term durability
Application
For medical, life preserver, outdoor, protective, shoes parts, ball, clothes, toys, infusion bed, water bags, industry and so on.
Specification
| Thickness | 0.1mm~2mm | Thickness Tolerance | ±10% |
| Width | 1000~1370mm | Surface Style | Glossy and Matte |
| Length | 100mm~1000mm (or more) | Color | Natural, Black, White, Red, Yellow, Transparent |
General Material Comparisons
| JUYONA Polyurethane Films | Flexible Vinyl(PVC) | Low Density Polyethylene | Natural Rubber | Neoprene | ||
| Hardness(Shore A) | 75-97 | 40-90 | 90-95 | 30-95 | 40-95 | |
| Specific Gravity | 1.1~1.3 | 1.3~1.4 | 0.9~1.0 | 0.9~15 | 1.2 | |
| Elongation (%) | 400~600 | 200~400 | 200~600 | 100~800 | 100~700 | |
| Tensile (PSI) | 4~10 | 1~3 | 1~2 | 1~4 | 1~3 | |
| Low Temp. Flex | Excellent | Fair-Poor | Good | Excellent | Good | |
| Resistance to: | ||||||
| Abrasion | Excellent | Fair | Poor | Good | Good | |
| Tearing | Excellent | Fair | Poor | Good | Good | |
| Oil | Good | Fair | Poor | Good | Good | |
| Ozone | Excellent | Excellent | Excellent | Poor | Good | |
| Water | Good- Excellent | Good | Excellent | Good | Good | |
| Heat Sealable | Yes | Yes | Yes | NO | NO | |
| Heat Bond | Yes | Yes | Yes | NO | NO | |
| Solvent Bond | Yes | Yes | Yes | NO | NO | |
| Ultrasonic Bond | Yes | Yes | Yes | NO | NO | |
| Thermoformable | Yes | Yes | Yes | NO | NO | |
Physical Properties
| Polyester base | Polyether base | |
| Tensile Properties (D638) | ||
| Modulus @ 100% strain (psi) | 800 | 1000 |
| Modulus @ 300% strain (psi) | 1800 | 2000 |
| Modulus @ break (psi) | 7000 | 7000 |
| Modulus of elasticity up to 10% strain (psi) | 30 | 35 |
| Elongation @ break (%) | 400 | 450 |
| Set @ break (%) | 30 | 35 |
| Set @ 100% strain (%) | 3 | 5 |
| Tear Properties | ||
| Die C (D624) pli | 425 | 400 |
| Split (D 1938) pli | 400 | 375 |
| Abrasion Resistance | ||
| Mg. weight loss/1000 cycles1000 gmload, H18 (ASTM C501) (mg) | 70 | 30 |
| Maximum Service Temperature | ||
| Continuous (°C) | -40~105 | -52~95 |
| Compression Properties (shape factor=0.56) | ||
| Set, Method A, 22hrs.70°C(D395) (%) | 11 | 12 |
| Set, Method B, 22hrs.70°C(D395) (%) | 18 | 23 |
| Durometer (D2240) (Shore A) | 85 | 85 |
| Thermal Properties | ||
| Melting Point Range (°C) | 182~204 | 176~198 |
| Specific Gravity (D792) | 1.2 | 1.14 |
| Yield Factors | ||
| Square Feet/Pound/Ml. Thickness | 160.3 | 168.8 |
| Vapor Transmission Rates (E96) | ||
| (Inverted @ 22±2°C grams weight loss/100 sq. in./24hrs. @mil thickness) | ||
| Distilled Water | 2 | 2.1 |
| Superunleaded gasoline | 4.7 | 20 |
| Humid Again Resistance | Fair to poor | Excellent |
| (90% relative humidity at160°F/70°C) | ||
| Notice: These values are based on the test of our present laboratory test specimens. | ||
**More information, please access our website:
https://www.taiwanpu.com/productInfo/PU%EF%BC%8BFilm/PU%EF%BC%8BFilm
Company Information
Packaging & Shipping
We Recommend
New Arrivals
New products from manufacturers at wholesale prices