polyurea paint for prilling tower wearable anticorrosion coating

 Characteristics    

The coating film is cured by reaction and absorption with air moisture then obtained high adhesive strength with substrate. The film is dense, flexible be able to adapt the certain deforming of substrate without cracks. It contains large amount of urea bond, biuret bond, urethane bond and hydrogen bond to get excellent physical properties and anticorrosion performance. It has high performance of acid resistance, alkali and salt resistance, waterproofing, temperature variation and chemical resistance. It is easy to apply with brush, roller or regular airless spray units. The service life can reach above 25 years if strictly confirm the regular application standard.

Specifications    

Adhesive strength                             3.5Mpa (or substrate broken)

Impact resistance                             ≥50kg·cm

Tensile strength                               17Mpa

Elongation                                         350%

Penetrate resistance                           2.3Mpa

Temperature variation                         -40------+160°C

Wear resistance(700g/500r)                12mg

Acid resistance 

40%H2SO4, 10%HCL, 30d            No rust, no bubbles, no peel done

Alkali resistance40%NaOH, 30d        No rust, no bubbles, no peel done

Salt resistance 100g/L, 30d            No rust, no bubbles, no peel done

Salt spray resistance, 1000h          No rust, no bubbles, no peel done

Oil resistance 

0#diesel, crude oil, 30d                    No rust, no bubbles, no peel done

Data of performance

Color                                                    Multiple colors as customers’ need

Luster                                                  half glazed

Density                                               1.08/cm3

Volume solid content                              81%±2%

VOC                                                     ≤176g/L  

Recommended dry film thickness              200-300um

Theoretical coverage                       0.24kg/sm(calculated by the above solids percentage and dry film thickness of 200 microns)

Practical coverage                                  allow appropriate loss rate 

Dry time                                              1-3h

Overcoating intervals                             min: 3h; max: 28h

Overcoating method                           airless spray, air spray, brush coating, roller coating

Flash point                                        63°C

Recommend procedures                  

 Application scope           Anticorrosion of fertilizer prilling tower in chemical industry.