polyurea polyaspartate floor coating

 Various of floor has been built in the national economy and it can be divided to many types based on different properties. Epoxy and carborundum floor is commonly used for its high strength and low price. But it can be easily damaged under impact since its low toughness. To solve the short service life of epoxy self-leveling floor, SWD developed aliphatic polyaspartic polyurea floor top coating. It has excellent flexibility and wear resistance, high adhesive strength with any brands floor material.                                                                                

Characteristics             High reaction activity, this coating has excellent fullness, tough, high impaction and shine gloss, with elastic and impact resistance, wearable and anti-slip. It has high performance of acid resistance, alkali resistance, anti- UV and weather resistance. 

Specifications

Adhesive force                                  9.3Mpa 

Tensile strength                                 9.5Mpa 

Elongation rate                                  352% 

Penetration resistance                      2.1Mpa

Temperature variation resistance           -40------+120℃ 

Surface hardness                               Shore A 90 

Wear resistance (750g/500r)               20mg 

Acid resistance

5%H2SO4 or 5%HCI,240d                 no rust antifade, no peel off 

Alkali resistance 5%NaOH,240d            no rust antifade, no peel off 

Salt resistance 30g/L,240d                 no rust antifade, no peel off 

Salt spray resistance,1500h                 no rust antifade, no peel off 

Oil resistance, engine oil 240h              no rust antifade, no peel off 

Water resistance 38h                      no bubbles, no wrinkle, antifade, no peel off                                                                               

Data of performance

Color                                 Multicolor as customer’s demand  

Luster                                 gloss 

Density                              1.07g/cm3 

Volume solid content            70%±2% 

VOC                                 ≤258g/L 

Recommended dry film thickness  100-300μm 

Theoretical coverage           0.18kg/sqm (calculated by the above solids percentage and dry film thickness of 100 microns) 

Practical coverage              Allow appropriate loss rate 

Tack free time                    1-3h(20 °C) 

Overcoating interval             min: 2h, max:8h (20°C) 

Overcoating method             airless spray, air spray, brush, roller 

Mix ratio                            A:B=1:1 (weight ratio) 

Flash point                         30°C±2°C

Recommend procedures             

Application scopes          Surface protection for various floors