Excellent wear-resistance welding material tungsten carbide copper Brazing Rod YD-5
Tungsten carbide copper Brazing Rod YD-5 it is made of by sintering tungsten carbide scrap and elastic matrix alloy,Outer layer of the special flux and coloring is marking scrap grade,the composition of sintering tungsten carbide scrap is mainly CO and WC,The hardness is HRA 89~91,tire body matal is Ni and copper alloy,strength can up to 690MPa, hardness HB≥160.
Material: tungsten carbide grits, steel pipe and copper binder
Sizes:
| Item | Size(mm) | Grain Size(mm) | Color |
| YD-9.5 | 9.5 | 9.5-6.5 | Dark Green |
| YD-8 | 8 | 8-6.5 | Dark Blue |
| YD-6.5 | 6.5 | 6.5-5 | Red |
| YD-5 | 5 | 5-3 | Yellow |
| YD-3 | 3 | 3-2 | Pink |
| YD-10 | 10 | 10-18 | Pale Green |
| YD-18 | 18 | 18-30 | Pale Blue |
| YD-30 | 30 | 30-50 | Pale Yellow |
overlaying process of tungsten carbide copper Brazing Rod YD-5,
The oxyacetylene butt, the operating process is as follows:
(1) clean up the workpiece, make the welding workpieces surface with metallic luster.
(2) the flat position of welding, therefore can use the appropriate clamping fixture for control of surfacing layer thickness, thick piece of available.
(3) with a neutral flame preheating, flame core not contact surface, the distance to 25 mm is advisable.
(4) carbide surfacing welding layer.With YD type electrode surfacing, the use of neutral flame (can be slightly carbonizing flame) tip is steady on the workpiece surface movement, the flame of the alloy electrode heating (be careful not to make flame cone tip contact alloy particles), tire body in the electrode alloy melt, carbide particles are also falling.Before the tire body of molten metal solidification, the particles arrange, can use left hand of the alloy electrode fingers, or another person holding a base electrode or pull rod on graphite rod in a quick stir particles, making them evenly aligned neatly.Surfacing layer thickness control according to the requirements of design.
(5) after the workpiece welding, where no ventilation, slow cooling, cannot quench, conditional usable asbestos blanket cover.
(6) the workpiece after cooling to room temperature, if necessary, grinding surface surfacing to required size and shape.
(7) clean up the workpiece, remove all splash, slag, etc.