RPEH 405 Antifouling Anti Rust Modified Epoxy Marine Anticorrosive Primer Paint For Boats

RPEH-405 High-Build Modified Epoxy Anticorrosive Primer (Iron Red)

Uses

As maintenance antirust primer for newly-built ships or old ships.

Color

Iron red

Application conditions

Airless spray

Recommended

Nozzle orifice

0.4~0.5mm

Nozzle pressure

100~150kg/cm²

Thinning ratio

0~10% .by weight

May be applied by spray, brush, or roller.

Thinner

FXH-4 Epoxy Thinner

Mixing ratio

Two components

base/curing agent=8/1 by weight

Pot life

Temperature

10°C

20°C

30°C

Pot life

10hrs

8hrs

6hrs

Film thickness

Dry film thickness 100μm/coat & Wet film thickness:185μm/coat

Solid content

74.2%

Specific gravity

1.45

Coverage rate

Theoretical

0.21kg/m2/100μm 0.148L/m2/100μm

Actual: depending on the surface treatment, environment and application methods

Dry time

Temperature

10°C

20°C

30°C

Dry to touch

2hrs

1.5hrs

1hrs

Dry to handle

14hrs

10hrs

8hrs

Coating interval

Min.

14hrs

10hrs

8hrs

Max.

—

—

—

Shelf life

12 months

Packing

A kit 22.5kg contains Part A 20kg and Part B2.5kg

Surface preparation

1.Remove salts and other water soluble contaminants with fresh water.

2.Remove oil in accordance with the solvent cleaning standard SSPC-SP1. 

3.Remove rust and scale by sand blasting to ISO Sa 2.5 (SSPC-SP10).

4.Remove the contaminants like dust with high pressure blower.

5.Confirm the surface clean and dry before working.

Coating system

Steel: Bare steel

Top coat: refer to our coating system