REFULGENCE PHOS COPPER TIN BRAZING ROD, 2% ~56% Ag FLUX COATED SILVER ROD

Specification: AWS BCuP-9
Composition(%): P 6-7, Cu balance, Sn,6.0-7.0 Other 0.15 max
Physical Constants:
Solidus(ºC):637
Liquidus(ºC):675
Brazing Range(ºC):643-693
DESCRIPTION:
AWS BCuP-9 is a ternary alloy of tin, phosphorus, and copper approaching the eutectic composition. It is very fluid at brazing temperature and should be used on well fitted joints. AWS BCuP-9 is low brazing temperature and narrow solidus-liquidus range makes it ideal for applications where temperature is a factor. It should be used with slow heating rates, such as in furnace brazing.
APPLICATIONS:
AWS BCuP-9 is used for joining of copper and copper alloys, such as brass or bronze. It is suitable for use on silver, tungsten, and molybdenum. It should not be used on ferrous or nickel alloys. On copper to copper applications, it is self-fluxing due to the fluxing action of the phosphorous content. Its low melting temperature makes it ideal for application on copper to brass where temperature and de-zincification is a factor.

REFULGENCE WORKSHOP

REFULGENEC-0 BCuP-2

PACKING & DELIVERY

Packing Details : Generally is 5kg/10kg shrink Packing, then 50kg wooden case and lastly 500kg/1000kg per pallet.

Delivery Details : 20 working days after got the ADV.

1. Picking out the defective one

2. 1kg packing in roll

3. 15kg packing per case

4. 600kg wooden case packing

5. Shipping from factory

6. Container loading

PARTNER & FRIENDS

ABOUT THE REFULGENCE

Q: Are you trading company or manufacturer ?

A: We are factory.

Q: How long is your delivery time?

A: Generally it is 5-10 days if the goods are in stock. or it is 15-20 days if the goods are not in stock, it is according to quantity.

Q: Do you provide samples ? is it free or extra ?

A: Yes, we could offer the sample for free charge but do not pay the cost of freight.

Q: What is your terms of payment ?

A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 30% T/T in advance ,balance before shippment.
If you have another question, pls feel free to contact us as below: