High Quality Pure Aluminum ingot for sale at factory prices

Share on:


Price:$300.00
Price in USD:Details

Quantity:


Product Overview

Description




Aluminum Ingot


 


Chemical Composition: al


Weight: 20/25kg


Al (Min): 99%-99.9%


Appearance: silvery white


 


Specifications


1,Aluminum ingot manufacture. 
2,high standard. 
3,High quality. 
4,Competitive price 
Brands : Al99.85,Al99.80,Al99.70



1,Aluminum ingot manufacture. 
2,high standard. 
3,High quality. 
4,Competitive price 
Brands : Al99.85,Al99.80,Al99.70



Products Name:Pure Aluminum Ingot99.9%


Chemical Composition: al


Weight: 20/25kg


Al (Min): 99%-99.9%


Place of Origin: Lesvos Island Greece


Appearance: silvery white


Aluminum ingot for remelting is produced by molten salt electrolysis method using alumina and cryolite. Products meet the national standard GB/T1196-2002. The surface of ingot is clean and smooth. 


Applications:


1. mainly used for melting ingot 
2. discontinuous melting with scrap 
3. easy control and operation 
4. fast melting


5. Used for industry such as automobile,pinning and weaving,electron broadly and so on       


 


The main models are as follows: AL99.90, AL99.85, AL99.70A, AL99.70, AL99.60, AL99.50, AL99.00, and below.    


Specifications:







































































































Grade



Chemical Composition   %



Al≥



impurities ≤



Si



Fe



Cu



Ga



Mg



Zn



Mn



others



Sum



Al99.9



99.90



0.50



0.07



0.005



0.02



0.01



0.025



-



0.010



0.10



Al99.85



99.85



0.80



0.12



0.005



0.03



0.02



0.030



-



0.015



0.15



Al99.7



99.70



0.10



0.20



0.010



0.03



0.02



0.030



-



0.030



0.30



Al99.6



99.60



0.16



0.25



0.010



0.03



0.03



0.030



-



0.030



0.40



Al99.5



99.50



0.22



0.30



0.020



0.03



0.05



0.050



-



0.030



0.50



Al99.00



99.00



0.42



0.50



0.020



0.03



0.05



0.050



-



0.050



1.00



 