Waterborne building Coating Inorganic ceramics antibacterial waterproof fireproof paint

Waterborne nano-alloy coating is an environmentally-friendly inorganic nano-ceramic coating specially designed for interior wall surface protection, with world-leading technology. Its main components are alumina and silica, and it does not contain formaldehyde or benzene. At the same time, it has excellent anti-fouling and anti-bacterial properties, Class A non-combustible fire, no smoke and odor, no harmful gas release, revolutionized in health, environmental protection, pollution-resistant waterproof, anti-bacterial fire, hard wear resistance and other performance indicators The technological breakthrough can greatly improve the quality of architectural coatings.

 Stronger anti-ultraviolet aging, providing environmentally-friendly coatings based on water-based nano-alloy resin, and developing various coatings such as light, semi-gloss and transparent according to various needs of customers.
It is a combination of decoration, stain resistance and mildew resistance, as well as imitation stone and imitation tile effect coatings. In addition to using various painting tools to create natural decorative effects, your concept can be fully realized.

A, B liquid mixing will have an exothermic reaction, and there will be an instantaneous gel phenomenon, which is normal. )
Component B contains alcohol and other active substances and has a pungent odor. When it is added to A, it will react. There is a short-term fever during the reaction. After 3-5 minutes, the odor disappears.

The ribs on the base are not sharpened, and the uneven parts need to be filled with putty to fill the flat.
 Coating construction
Check the surface putty during the construction of the paint should be firm and firm, and must not be chalked, peeled and cracked. After the putty is dried, it should be smooth and smooth and cleaned.
 Penetrant construction

 roller coating with short-haired rollers, uniform roller coating, surface drying may leave roller marks. This is a normal phenomenon. Under the condition of temperature not lower than 15 °C, natural drying for more than 12 hours can be used for primer construction. 

  Primer construction 

After the penetrant is dry, the primer is applied with a short-haired roller. During the roller coating process, it does not penetrate the bottom, does not sag, does not show the brush pattern, and naturally dries for 12 hours under the condition of temperature not lower than 15 °C. The above can be used for topcoat construction.
 Topcoat construction

 Under the condition of temperature not lower than 15 °C, use short-hair roller construction to ensure that the roller coating process does not penetrate the bottom, does not sag, and does not show the brush pattern. Do not dilute with water during the application process. The secondary application must be carried out after the coating is dry. After the curing, the secondary coating cannot be carried out. The interval should be controlled within 1-2 hours. (The surface is not sticky, the film can be scratched)

1. Putty should be dried for more than 7 days before it can be used as a closed penetrant.
2. The closed penetrant can be used as a primer after more than 12 hours of completion.
3, the primer can be used for more than 12 hours to finish the topcoat.
4. The top coat is a two-component paint. Add B to A. The mixing time should be 15 minutes, and it can be placed for 15 minutes.
         If the mixing time is not enough, there may be quality problems such as cracking.
5. Two coats of paint are applied, and the interval between the two passes is 2-4 hours.
         If the time interval is too long, the coating may fall off.
6. After the topcoat is mixed, the use time should not exceed 6 hours, and it is related to temperature. The higher the temperature, the shorter the use time. More than 30 degrees of use should not exceed 4 hours.
         If the application time is too long, the coating will thicken and work, which will cause the coating to crack.

 It is mainly used in places where the wall coating has hard wear resistance, antibacterial and mildew resistance, stain resistance, waterproof and UV resistance, such as the inner wall of the student building, the indoor environment of the amusement park, kindergartens, schools and other places.