New Material Abrasion Resistance Cobalt Chromium Molybdenum Dental Alloy

DAMCAST NB

A high strength nickel chrome with beryllium alloy as defi ned by ISO9693,for restoration of Pocelain-Fused-to-Metal,is compatible with most popular procelain and offers superior bond strength

Composition: Ni76%,Cr15%,Mo5%,Be1.7%,Al2% others3%

Technical Data: 

Colour:white 

Melting Range:1232-1288℃ 

Yield Strength:552Mpa 

Elongation:11% 

Density:7.9 g/cm3 

Coeffi cient of the Liner Expansion(25-500℃): 13.8 X 10-6K-1

DAMCAST NP

A b i o c o m p a t i b l e , N i c k e l Chrome dental alloy,beryllium free,as defined by ISO22674 for restoration of Pocelain- Fused-to-Metal,designed for the technician who demands easy application from a non- beryllium alloy.

Composition: Ni61%,Cr25%,Mo11%,Si1.5% others3%

Technical Data: 

Colour:white 

Melting Range:1310-1360℃ 

Yield Strength:320Mpa 

Elongation:19% 

Density:8.3 g/cm3 

Coeffi cient of \\theLiner Expansion(25-500 ℃): 14.1 X 10-6K-1

DAMCAST PS

A cobalt chrome alloy,nickel & beryllium free,as defined by ISO22674,for restoration of removable framework and partial dentures.

Composition: Co64%,Cr29%,Mo6%,others3%

Technical Data: 

Colour:white 

Melting Range:1240-1340℃ 

Yield Strength:520Mpa 

Elongation:6% 

Density:8.3 g/cm3 

Modulus of Elasticity:220Gpa

DAMCAST CC

A biocompatible,Cobalt Chrome dental alloy,nickel & beryllium free, as defi ned by ISO22674,for restoration of Pocelain-Fused-to-Metal.

Composition: Co61%,Cr25%,Mo6%,W5%,others3%

Technical Data: 

Colour:white 

Melting Range:1290-1370℃ 

Yield Strength:530Mpa 

Elongation:4% 

Density:8.5 g/cm3 

Coeffi cient of the Liner Expansion(25-500℃): 14.1 X 10-6K-1

DAMCAST soft

A nickel base alloy as defi ned by ISO22674,designed for the production of high quality full crowns bridges,inlays,acrylics and composite restorations.

Composition: Ni75%,Cr5%,Cu12.5%,Sn5.5% others3%

Technical Data: 

Colour:white 

Melting Range:1230-1330℃ 

Yield Strength:260Mpa 

Elongation:19% 

Density:8.4 g/cm3

DAMCAST TS

Nickel-Cobalt dental alloy, as defined by ISO22674,ideal for restoration partial denture framework

Niminal composition: Ni balance Co8% Cr16% Mo5% Be1.5% others 10% max

Technical Data: 

Density:8.0g/cm 3 

Elongation: 5% 

Melting Range:1270-1320℃ 

Casting Temperature:1400℃ 

Vickers Hardness:360 

Modulus of Elasticity:230Gpa

Time of shipment:

1. Express: 2 working days after the receipt of the payment by the aircraft.

2. Vessel: Shipping within 7 working days after receipt of payment by ship.

3 shows. 2 - 1 weeks of goods without inventory

Main way of expression:

EMS:3 ~ 15 days