PA66 GF15,Good Mechanical Properties,Polyamide66,Reinforced With 15% Glass Fiber

polyamide 66, reinforced with 15% of glass fibre, for injection moulding. This grade offers an excellent combination between thermal and mechanical properties.

• Good Dimensional Stability


• Good Flow


• Good Mold Release


• Translucency

Bearing cages; Connectors; Gear wheels; Pulleys; Switch, Plug, Control & Sockets; White appliances

 PA (nylon) materials must be properly dried in order to provide parts with optimum strength and toughness. Nylon materials are hygroscopic and will become degraded by excessive moisture during the injection molding process. Product is supplied in moisture-protected containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 4-6 hours is generally sufficient, but final moisture content must be less than 0.2% 

Melt Temperature: 250-270 °C 
Mold Temperature: 70-90 °C but temperatures of as low as 45 °C and as high as 105 °C can be used where applicable;
Injection Pressure: 60-90MPa.

 FILL RATE

Fast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate.

 NOTE

Although all statements and information in this publication are believed to be accurate and reliable, they are presented gratis and for guidance only,  and risks and liability for results obtained by use of the products or application of the suggestions described are assumed by the user. No warranties of any kind, either express or implied , including warranties of merchantability or fitness for a particular purpose, are made regarding products described or designs, data or information set forth.