GENERAL INFORMATION | ||||||
BRAND: LG CHEM | GRADE:ESTER TYPE TPE KEYFLEX BT 1063D | |||||
FEATURES: | 1.HIGH MODULUS | 2.GENERAL PURPOSE | ||||
COLOR: | BLACK COLOR | |||||
FORM: | PELLETS | |||||
PROCESSING METHOD: | INJECTION MOLDING |
Properties | Test Condition | Test Method | Unit | Typical Value | |||
Physical | |||||||
Specific Gravity | ASTM D792 | - | 1.23 | ||||
Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 1.3 ~ 1.7 | ||||
Melt Flow Rate | 230℃/2.16kg | ASTM D1238 | g/10min | 24 | |||
Water Absorption | 23℃, 24hrs | ASTM D570 | % | 0.3 | |||
Mechanical | |||||||
Tensile Strength, 2mm | ASTM D638 | ||||||
@ Yield | 50mm/min | kg/cm2 | 190 | ||||
@ Break | 50mm/min | kg/cm2 | 500 | ||||
Tensile Elongation, 2mm | ASTM D638 | ||||||
@ Yield | 50mm/min | % | |||||
@ Break | 50mm/min | % | 650 | ||||
Flexural Strength, 6.4mm | 15mm/min | ASTM D790 | kg/cm2 | ||||
Flexural Modulus, 6.4mm | 15mm/min | ASTM D790 | kg/cm2 | 3,300 | |||
Tear Strength @ Break | 50mm/min | ASTM D624 | kg/cm | 160 | |||
IZOD Impact Strength, 6.4mm | ASTM D256 | ||||||
(Notched) | 23℃ | kg·cm/cm | No break | ||||
-40℃ | kg·cm/cm | 6.5 | |||||
Shore Hardness | Shore D | ASTM D2240 | - | 61 | |||
Shore Hardness | Shore A | ASTM D2240 | - | ||||
Thermal | |||||||
Melt Temperature @ Peak | ASTM D3418 | ℃ | 212 | ||||
Heat Deflection Temperature, 6.4mm | ASTM D648 | ||||||
(Unannealed) | 4.6kg | ℃ | 111 | ||||
Flammability | UL94 | ||||||
1.5mm | class | HB | |||||
3.0mm | class | HB | |||||
Electrical | |||||||
Comparative Tracking Index(CTI) | Solution A | IEC 60112 | Volts | 600 | |||
Surface Resistivity | IEC 60093 | Ohm | |||||
Volume Resistivity | 23℃ | ASTM D257 | Ohm·m | >E13 | |||
Dielectric Strength, 1mm | 23℃ | ASTM D149 | kV/mm | 26 | |||
Dielectric Constant (106 Hz) | 23℃ | ASTM D150 | sec |