BRAND:BLUESTAR | GRADE:403M-G20 | ||||
MATERIAL: | PBT+20% GLASS FIBER AND MINERAL REINFORCED | ||||
FEATURES: | 1. FLAME RETARDANT | 2. HIGH THERMAL STABILITY AND GOOD PROCESSABILITY | |||
COLOR: | WHITE | ||||
FORM: | PELLETS | ||||
METHOD: | INJECTION MOLDING |
Properties | Test Method | Unit | Typical Value | ||
Physical | |||||
Specific Gravity | ISO1183-1-2012 | g/cm³ | 1.56 | ||
Melt Flow Rate,250℃/2.16kg | ISO1133:2011 | g/10min | 20 | ||
Molding Shrinkage (Parallel) | ISO 294-4 | % | 0.4 | ||
Molding Shrinkage (normal) | ISO 294-4 | % | 1.1 | ||
Mechanical | |||||
Tensile Stress at break,10mm/min | ISO 527-2 | MPa | 110 | ||
Tensile Strain at break,10mm/min | ISO 527-2 | % | - | ||
Flexural Strength,2mm/min | ISO 178:2010 | MPa | 180 | ||
Flexural Modulus,2mm/min | ISO 178:2010 | MPa | 6800 | ||
Charpy Impact,Notched, 23℃ | ISO 179 | KJ/m² | 7 | ||
Charpy Impact,Unnotched, 23℃ | ISO 179 | KJ/m² | 55 | ||
Thermal | |||||
Heat Deflection Temperature,1.80Mpa, 3.2mm, unannealed | ISO 75-1/-2 | ℃ | 195 | ||
Heat Deflection Temperature,0.45Mpa, 3.2mm, unannealed | ISO 75-1/-2 | ℃ | 202 | ||
Flammability | |||||
Flammability,0.8-3.2mm | UL94 | - | V-0 | ||
Coefficient of linear thermal expansion,longitudinal(23-80)℃ | ISO 11359-1/-2 | E-6/K | 30-40 | ||
Electrical | |||||
Volume Resistivity | IEC 60093 | Ω.cm | 1.0×1016 | ||
Dielectric Strength, in oil | IEC 60243-1 | KV/mm | 20 | ||
Relative Dielectric Constant,50Hz | IEC60250 | - | 3.3 | ||
Dissipation Factor,50/60Hz | IEC60250 | - | 0.02 | ||
Comparative Tracking Index | IEC60112 | V | - |