Item | Test data | Unit | Test method | Test conditions |
Density | 1040 | kg/m3 | ISO 1183:1987 | |
Water absorption | <0.1 | % | ISO 62:1999 | |
Melt flow rate | 3.8 | cm3/10min | ISO 1133:1997 | 200°C/5kg |
Process shrinkage | 0.4-0.6 | % | ISO 294-4:1997 | |
Charpy impact strength | 15 | kj/m2 | ISO 179:1993 | 1eU |
Tensile modulus | 3300 | MPa | ISO 527-2:1993 | 1mm/min |
Elongation | 3 | % | ISO 527-2:1993 | 50mm/min |
Tensile strength at break | 55 | MPa | ISO 527-2:1993 | 50mm/min |
Ball indentation hardness H | 150 | N/mm2 | ISO 2039-1:1993 | 358N/30s |
Bending strength | 100 | MPa | ISO 178:1993 | 2mm/min |
HDT | 84 | °C | ISO 75-2:1993 | 1.8MPa |
Linear coefficient of thermal expansion | 0.8-1.0 | K-1 | DIN 53 752 | (23-80)°C |
Heat conduction | 0.16 | W/mK | DIN 52 612 | |
Vicat softening point | 93 | °C | ISO 306:1994 | B50/oil |
Flame retardance | 94HB | Class | UL-Standard 94 | >1.4mm |