PROPERTY | TEST METHOD | UNITS | VALUE |
Density | ISO 1183 | g/cm³ | 1.20 |
Water Absorption, 50% RH, 23℃ | ISO 62 | % | 0.15 |
Water Absorption, saturation, 23℃ | ISO 62 | % | 0.35 |
Tensile Strength at Yield 50mm/min | ISO 527 | MPa | >60 |
Nominal Strain at break 50mm/min | ISO 527 | % | >100 |
Tensile Modulus 1mm/min | ISO 527 | MPa | 2300 |
Flexural Strength 2mm/min | ISO 178 | MPa | 90 |
Flexural Modulus 2mm/min | ISO 178 | MPa | 2300 |
Charpy Impact, notched 23℃, 3.0mm | ISO 179/1eA | KJ/m² | 75 |
Izod Impact, unnotched 23℃, 3.0mm | ISO 180/1U | KJ/m² | NB |
Izod Impact, notched 23℃, 3.0mm | ISO 180/1A | KJ/m² | 70 |
Vicat Softening Temperature, rate B/120 | ISO 306 | ℃ | 145 |
Temperature of Deflection under Load (type A), 1.8MPa, flat | ISO 75-2 | ℃ | 127 |
Thermal Conductivity | ISO 8302 | W/m.℃ | 0.2 |
Coefficient of Linear Thermal Expansion, 23-55℃ | ISO 11359-2 | 1/℃ | 7×10-5 |
Ball Pressure Test 125± 2℃ | IEC 60695-10-2 | - | Pass |
Volume Resistivity | IEC 60093 | Ohm.cm | >1015 |
Dielectric Strength, in oil, 3.2mm | IEC 60243-1 | kV/mm | 18 |
item | value |
Warranty | More than 5 years |
After-sale Service | Online technical support, Onsite Installation, Onsite Training, Onsite Inspection, Free spare parts, Return and Replacement, Other |
Project Solution Capability | graphic design, 3D model design, total solution for projects, Cross Categories Consolidation, Others |
Application | Building & Construction |
Design Style | Modern |
Place of Origin | China |
Guangdong | |
Brand Name | LEXAN |
Model Number | LX |
colour | clear |
shape | panel |
material quality | polycarbonate |
size | customized |
Target audience | ALL |
OEM | accept |
Новинки товаров от производителей по оптовым ценам