Оригинальная упаковка частиц ударопрочного полистирола HIPS
1 600,00 $
Сохранить в закладки 60257611684:
Properties | ASTM method | Test Condition | Unit | Typical Value |
Specific Gravity | D542 | --- | --- | 1.046 |
Melt Flow Index | D1238 | 200°C,5 kg load | g/10 min | 4.6 |
Tensile Strength at Yield | D638 | 23°C,1/8” Sample | kg/cm2 | 300 |
Elongation at Break | D638 | 23°C,1/8” Sample | % | 40 |
Izod Impact Strength | D256 | 23°C,A method,notched1/8”×1/2”×5/2” | kg/m2 | 9.5
|
Vicat Softening Temperature | D1525 | 1 kg load,3 mm Thick ( 120°C/hr ) | °C | 97 |
Flammability | UL-94 | 1/16” Sample | File No.E50263 | 94HB |
Residual SM monomer | --- | --- | ppm | <300 |
Yellow Index | --- | --- | --- | -6 |
Grades | GH600 | GH825 | GH860 |
| MFR g/10min g/10min | 6.0 | 7.5 | 8.0 |
| Rwsidual Monomer mg/kg | ≤ 800 | ≤ 800 | ≤ 800 |
| Vicat softening Point °C | ≥ 88 | ≥ 87 | ≥ 88 |
| Notched Izod Impact Strength KJ/m2 | ≥ 7.3 | ≥ 8.9 | ≥ 6.0 |
| Tensile Stress Yield MPa | ≥ 18 | ≥ 19 | ≥ 16 |
Tensile Straint at Break % | ≥30 | ≥ 30 | ≥ 30 |
| -// | - | ||
| Manufactures | Guangzhou | Guangzhou |