We are capable of providing stainless steel spheres/balls almost as per your specific requirements. Products include hollow stainless steel spheres (ranging from 6mm to 2500mm in diameter), available for delivery if we have it in stock or delivered within 15 days. Wall thickness of spheres varies from 0.4mm to 3mm. Shaped by water pressure, our products could be mirror polished without any seams noticeable on the surface; meanwhile, welding and then sandblasting spheres is a another way to produce mirror polished spheres also without detectable traces on the spheres. Having been offering services for our customers worldwide, a variety of products also fall under many categories of our products. Staidness steel spheres, hollow or solid, of all sizes are our major products, and brass and bronze balls come along. Hollow reflective stainless steel spheres of enormous sizes are amongst the top sales in our products. Perforated stainless steel spheres or sculptures of 304 or 316 are also our hot products. Not to mention we have done considerable amount of drilled stainless steel balls or spheres with holes of many sizes. Our products are of professional and advanced technology with cost-effective craftsmanship and favorable delivery time. 

 

 

 

 

 

Types 304 and 304L exhibit excellent resistance to corrosive environments such as the chemical, textile and petroleum industries.Type 304 and 304L are found suitable in the food and dairy industries as well as excelling in rural and industrial atmospheric exposure.By reducing the carbon content in Type 304L, welding operations will not cause carbide precipitation that can lead to inter-granular corrosion. The maximum temperature  to which Type 304 can be exposed continuously without appreciable scaling is about 1650 °F (899 °C).For intermittent cyclic exposure, the maximum exposure temperature

is about 1500 °F (816 °C).Type 304 is non-hard enable by heat treatment.Annealing: Heat to 1900 – 2050 °F (1038 – 1121 °C), then cool rapidly.Thin strip sections may be air cooled, but heavy sections should be water quenched to minimize exposure in the carbide precipitation region.Stress Relief Annealing: Cold worked parts should be stress relieved at750 °F (399 °C) for 1/2 to 2 hours.High hardness and strength  are achieved through cold working. In the annealed condition, Types 304 and 304L are very ductile and can be cold worked easily by roll forming, deep drawing, bending, and other common fabricating methods. Since the material work hardens rapidly, in-process annealing may be necessary to restore ductility and to lower hardness.Types 304 and 304L can be readily formed and drawn. The higher nickel versions of  Type 304 are well suited to severe forming applications involving multi-draw operations and forming of complex shapes. This is largely due to its combination of lower strength and lower work hardening rate. 

 

Composition ranges for 304 grade stainless steel

Grade		C	Mn	Si	P	S	Cr	Mo	Ni	N
304	min. max.	- 0.08	- 2.0	- 0.75	- 0.045	- 0.030	18.0 20.0	-	8.0 10.5	- 0.10

 

Mechanical properties of 304 grade stainless steel

Grade	Tensile Strength (MPa) min	Yield Strength  0.2% Proof (MPa) min	Elongation (% in 50mm) min	Hardness
				Rockwell B (HR B) max	Brinell (HB) max
304	515	205	40	92	201

 

 

Physical properties of 304 grade stainless steel in the annealed condition

 

Grade		Elastic  Modulus  (GPa)	Mean Coefficient of  Thermal Expansion (μm/m/°C)			Thermal Conductivity (W/m.K)		Specific Heat  0-100°C  (J/kg.K)	Electrical Resistivity (nΩ.m)
			0-100°C	0-315°C	0-538°C	at 100°C	at 500°C
304/L/H	8000	193	17.2	17.8	18.4	16.2	21.5	500	720

 

 

 

Grade specifications for 304 grade stainless steel

 

Grade	UNS No	Old British		Euronorm		Swedish SS	Japanese JIS
		BS	En	No	Name
304	S30400	304S31	58E	1.4301	X5CrNi18-10	2332	SUS 304

 

 

 

Physical capability of stainless steel balls
CAPABILTY MODEL	201	302	304	316
Tensile strength	100,000 - 180,000 psi	100,000-180,000 psi	100,000 - 180,000 psi	90,000 psi
Yield strength	50,000 - 150,000 psi	50,000-150,000 psi	50,000 - 150,000 psi	45,000 psi
Tensibility	55-60%	55-60%	55 - 60%	35%
Modulus of Elasticity	29,000,000 psi	29,000,000 psi	29,000,000 psi	28,000,000 psi
Density	280lbs/cubic inch	286lbs/cubic inch	286 lbs/cubic inch	290lbs/cubic inch