Item | Test Method | Result |
Transparency | ASTMD 1003 | >98% |
UV Irradiation 1000 hours | ASTMD 4329-99 | YI<1.8 |
85℃+85% RH 1000 hours | IEC 60068-2-78 | YI<2 |
Shrinkage Rate | ASTMD 1204 | MD<3.0% TD<3.0% |
Peel Strength to Glass | GB/T 2790-1995 | >74N/cm |
Peel Strength to Backsheet | >62N/cm | |
Gel Content (Crosslinking) | ASTMD 2765 | >75% |
Tensil Strength | ISO 527-03 | 18.6mpa |
Elongation at Break | 555% | |
Water Absorption | GB/T 1034-1998 | <0.1% |
Volume Resistivity | GB/T 1410-2006 | 1.3*1015 |
Thickness | 0.15mm | |
Width | 670/820/990/1000mm | |
Length | 150m/100m | |
width and length can be customized | ||
Item | Vacuation time | Lamination Temp. | Solidify time | |||
SUN-T | 4-6 mins | 130-135℃ | 10-15 mins | |||
Remark:You should do cross-ling rate performance testing according to the different temperature of laminated equipment, the different size and quantity of solar module. | ||||||