BAlSi 4 паста алюминием сплав сварочная паста

Specifications

Aluminum brazing paste 

DIN EN 1044: AL 104 

DIN 8513: L-Al Si 12 

EN ISO 3677: B-Al 88 Si – 575/585 

AWS A 5.8: B Al Si - 4

Composition, typical analysis (% w/w): 

Mechanical and physical properties: 

Working temperature: 590°C 

Melting range: 577 – 582°C 

Specific gravity: 2.7 g/cm³(Metal content) 

Characteristics/Applications: 

Capillary active brazing alloy for structure matching and tonal joints of aluminum and rolled/cast aluminum alloys. The Mg content must be≤3%. The solidus temperature should be>630°C. Not suitable for joints that are to be eloxadized. This brazing alloy is also suited for joints of aluminum with Cr-Ni-steel. The flux residues have to be removed after brazing. 

Heat sources: 

Inert gas furnace (N2, cracked ammonia), acetylene torch (indirect heating

Storage: 

Keep sealed, under stable temperatures in dry rooms. Optimum temperature range is between 5 and 20°C. Stir well before use. 

Shelf life: 

6 Mo. in pots

Availability: On request